Abrasion and Impact Resistance Welding Skid Bars, Heavy Duty Buckets Laminated Skid Blocks, White Cast Iron Laminted Wear Block Skid Bars 700 HB / 63 HRC 15/3CrMo Chrome White Iron Domite Skid Bar, Bucket Wear Parts, Bimetallic Skid Bars With Dippers Edges, Skid Bars For Ore Mining & Coal Mining Abrasion and Impact Resistance Welding […]
White Iron Wear Bar, Bimetallic Wear Bar, White Iron laminated blocks wear bars for wear mining protection, Weldable casting wear bars, high chromium 700HB 63HRC white iron wear bar for mining machine parts, Abrasion-proof wear bars blocks China supplier
White Iron Wear Bar – Wear bar is a combination of high chromium (700 brunell) white iron bonded to a mild steel weldable backing plate. Wear bars and blocks are available in thicknesses ranging from 25mm to 100mm, widths from 25mm to 300mm wide and in varying lengths.Popular for use in rock box protection, impact areas and transfer points, bars can be provided with Nelson studs with size and and location to suit.
Available in a wide range of sizes, can be used in a combination of our standard lengths to create layouts and patterns. Perfect for corners, edges and hard to reach places, use Bimetallic Wear Bar and Blocks wherever you need impact and wear resistance.
Wear Bars are available in thicknesses ranging from 25mm to 100mm, widths from 25mm to 300mm wide and in varying lengths. They can be stud bolted to suit fitment needs. They offer superior wear life when compared to conventional alloys such as manganese steel, Ni-hard, Q&T bars and clad overlay strips.
Wear Bars offer a cost effective solutions to wear problems.
laminated 700 HB Wear-resistant Parts are the ideal solution for impact and high abrasion in the following industries:
Earthmoving equipment and transhipment companies
Mineral processing industry
laminated 700 HB / 63 HRc Wear-resistant Parts benefits:
Lower operating costs
Longer Service when compared to conventional materials
Improved product efficiency
Increased equipment availability
Applications mining bimetallic wear bar:
Chutes and liners
Suction mouth dredging industry
Protection of tunnelboring machines
Protection dragheads dredging industry
Protection earth moving equipment / shovels / buckets
bimetallic composites is an exceptional laminated product that is resistant to impact and abrasion while retaining ductile characteristics by bonding High-chromium cast iron onto a mild steel backing plate.The bonding shear strength is over 210Mpa and will not separate.
High-chromium cast iron which hardness is Min.63HRC provides very high wear resistant qualities,while the steel backing plate acts as a meaning of absorbing high impacts and allows easy to use and install with no pre or post heating when welding.
|Part No.||Size||A(mm)||B(mm)||C(mm)||D(mm)||E(mm)||Unit Weight(kgs)|