White Iron Laminated Wear Plates

White Iron Laminated Wear Plates, Bimetallic chrome white iron brazed wear plates, Laminated Wear Plate Wear Liners Bimetallic Chromium Carbide Wear Plates, laminated 700 HB / 63 HRc Wear Plates, Wear-resistant plates parts, Domite 700bhn High Chrome Cast Iron Wear Plate China supplier

Laminated Wear Plates – It is a combination of high chromium white iron metallurgically bonded to a mild steel backing plate.

Advantages:
Hardness: 700BHN (HRC62-66)
Thickness: 12mm to 70mm
Large sizes available(600mmX900mm)

Applications:
Chutes/Hoppers/Bins
Earthmoving Equipments
Transfer Points
Truck Beds
Rock Box Edges
Impact Walls
Screen Plates

Material: Chrome white iron wear casting vacuum brazed onto mild steel base.
The smallest thickness for wear material we can make is 6mm.

Advantage:
1. Hardness: 63HRC/700BHN. The usage life is at least 2 times higher compared with overlay/hardfacing wear plates, at least 7 times longer than A.R type steels 360/400BHN. The thicker ones such as 20mm above wear, the usage life is much more longer. The wear resistance performance is the same from wear surface to the welding face.
2. Wear surface is very smooth and flat, media is not easy to stick on.
3. It can make with different shapes and sizes.
4. Better cost-efficient. Unit price is about USD5.5—USD7.5 per kilogram.

Weakness: for big sheet size, wear casting could be joint ones, not a whole sheet. For example, wear plate 1443x349x25/6mm(25mm wear, 6mm base), the wear material will be jointed with 4pcs, and mild steel base will be joint with 2pcs, joint gap is below 2mm

Suitable for use in chutes, hoppers, bins, liners, impact walls, rock boxes and a variety of other applications.
Very easy to use, no pre or post heating when welding. overlay wear plates

700 HB Wear-resistant Parts are the ideal solution for impact and high abrasion in the following industries:
Earthmoving equipment and transhipment companies
Cement plants
Dredging industry
Recycling industry
Mineral processing industry

laminated 700 HB / 63 HRc Wear-resistant Parts benefits:
Lower operating costs
Longer Service when compared to conventional materials
Increased production
Improved product efficiency
Increased equipment availability

Applications laminated 700 HB / 63 HRc Wear-resistant Parts:
Chutes and liners
Suction mouth dredging industry
Protection of tunnelboring machines
Shredder tips
Protection dragheads dredging industry
Protection earth moving equipment / shovels / buckets

Request a Quote

Affordable Price
OEM Parts Available

Payment Easy
Worldwide Delivery

Quality Guaranteed
Bulk Discount

Product Range

Type	Item No.	Size	Dimension(mm)					N.W.(kg)
Type	Item No.	mm	A	B	C	D	E	N.W.(kg)
Standard	WP 200-18	200x200x18	200	200	12	6	18	5.7
	WP 200-20	200x200x20	200	200	14	6	20	6.3
	WP 300A	300x150x20	300	150	14	6	20	7
	WP 250	250x250x20	250	250	14	6	20	9.8
	WP 300C	300x300x18	300	300	12	6	18	12.7
	WP 300B	300x300x20	300	300	14	6	20	14.1
	WP 305	305x150x24	305	150	18	6	24	8.6
	WP 300C	300x150x25	300	150	19	6	25	8.8
	WP 300D	300x300x25	300	300	19	6	25	17.7
	WP 445	445x445x25	445	445	19	6	25	38.9
	WP 301	301x200x28	301	200	18	10	28	13.2
	WP 294A	294x144x30	294	144	20	10	30	10.2
	WP 294B	294x294x30	294	294	20	10	30	20.4
	WP 300E	300x150x30	300	150	20	10	30	10.6
	WP 300F	300x300x30	300	300	20	10	30	21.2
	WP 372	372x372x28	372	372	20	8	28	30.4
	WP 300G	300x300x50	300	300	40	10	50	35.3
	WP 300H	300x148x50	300	148	40	10	50	17.4
	WP 206	206x203x58	206	203	38	20	58	19
Trapezoidal	WPt 190	190×212.5×25	190	212.5	17	8	25	7.9
Trapezoidal	WPt 241	241×290.5×30	241	290.5	22	8	30	19.5