Wear Resistant Chute Wear Liner Plate – Laminated Wear Plates combine very high wear resistant qualities of a high chrome cast iron (ASTM A532, 700 BHN/63 HRc) with a weldable & high impact toughness mild steel.
Wear Resistant Chute Wear Liner Plate Advantege:
exceptionally resistant to impact and abrasion while retaining
Wear Resistant Chute Wear Liner Plate Main matterial:
high chrome cast iron( ASTM A 532, abrasion resistance) + mild steel backing plate( impact resistance)
Wear Resistant Chute Wear Liner Plate Mechanical Property
1) Tensile Strength 630Mpa Min.
2) Shearing Strength 250Mpa Min.
3) Hardness 63 HRC
And we can produce according to your drawings, sizes and specific needs.
Wear Resistant Chute Wear Liner Plate Advantages:
Better wear resistance performance, Durable, Cost effective, Excellent quality, Good service
Item Size(mm) N.W.(kg)
WP 200 200X200X20 6.3
WP 300A 300X150X20 7.0
WP 250 250X250X20 9.8
WP 300B 300X300X20 14.1
WP 300C 300X150X25 8.8
WP 300D 300X300X25 17.7
WP 445 445X445X25 38.9
WP 301 301X200X28 13.2
WP 294A 294X144X30 10.2
WP 294B 294X294X30 20.4
WP 300E 300X150X30 10.6
WP 300F 300X300X30 21.2
WP 372 372X372X28 30.4
WP 300G 300X300X50 35.3
WP 300H 300X148X50 17.4
WP 206 206X203X58 19.0
Some of our products and services:
Wear plates, wear liners
Chocky bars and wear buttons
Wear blocks, wear bars
Custom made wear liners
Bucket repair and protection
Full Fabrication services
Sugar mill hammer tips
Drilling, milling or machining
Fast service and timely delivery
Available in various sizes or made to customer requirements, wear plates can be used in a combination of different sizes to create optimum layouts that provide the greatest impact and wear protection.
Wear Plates can be simply welded onto a surface with no pre or post heating.
Ideal for chutes,hoppers,bins,liners,impact walls,rock boxes and a lot other applications,wear plates help to Reduce downtime and Increase output.
the chrome-moly white iron with finished minimum hardness of 63HRC or 700 BHN, Delivers maximum abrasion protection, while the steel baCking plate absorbs High impact and facilitates ease of fitting and use.
the bonding shear strength is over 30,500 psi (or 210 Mpa) and will not separate.
Bucket Tooth History
Bucket Fill or Cycle Time? Which is More Important?
CATERPILLAR BOLT-ON SIDE PROTECTOR
White Iron Laminated Wear Plates
White Iron Laminated Wear Plates, Bimetallic chrome white iron brazed wear plates, Laminated Wear Plate Wear Liners Bimetallic Chromium Carbide Wear Plates, laminated 700 HB / 63 HRc Wear Plates, Wear-resistant plates parts, Domite 700bhn High Chrome Cast Iron Wear Plate China supplier Laminated Wear Plates – It is a combination of high chromium white […]
Overlay Wear Plates
Overlay Wear Plates, Wear Resistant Hardfacing Steel Plate, Chromium Overlay Wear Plate for Impact Walls, Overlay Chromium Carbide Bimetallic Wear Plate, Chromium Carbide Overlay Plate Liner, 3+3, 4+6, 10+8, 12+17 Wear Plate, 550HB-650HB Wear resistant plate China Supplier Overlay Wear Plates – OVERLAY-PLATE is welded by Chromium carbide overlay on a mild steel backing plate. […]